Phase formation in mixed TiO2-ZrO2 oxides prepared by sol-gel method
2011
Pure titania, zirconia, and mixed oxides (3—37 mol.% of ZrO2) are prepared using the sol-gel method and calcined at different temperatures. The calcined samples are characterized by Raman spectroscopy, X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption porosimetry. Measurements reveal a thermal stability of the titania anatase phase that slightly increases in the presence of 3—13 mol.% of zirconia. Practically, the titania anatase-rutile phase transformation is hindered during the temperature increase above 700 C. The mixed oxide with 37 mol.% of ZrO2 treated at 550 C shows a new single amorphous phase with a surface area of the…
Effect of the dopant selection (Er, Eu, Nd or Ce) and its quantity on the formation of yttrium aluminum garnet nanopowders
2008
Abstract Hydroxide precursors, synthesized using the co-precipitation method, were calcined for 1 h at the temperatures of 900, 1000 and 1100 °C, respectively, and heated directly to 1500 °C to produce various Y 3 Al 5 O 12 (YAG) nanopowders with different doping quantities of erbium, europium, neodymium and cerium. All samples were investigated using thermo-gravimetry (TG) and differential thermal analysis (DTA), field emission gun-scanning electron microscopy (FEG-SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). TG and DTA experiments were performed from room temperature up to 1500 °C; the weight loss curves combined with the presence of exo- and endo-thermal even…
Co-precipitation synthesis of neodymium-doped yttrium aluminium oxides nanopowders: Quantitative phase investigation as a function of joint isotherma…
2007
Abstract Neodymium-doped yttrium aluminium nanopowders with nominal Nd:Y:Al ratio equal to X:3–X:5 (where X = 0, 0.006, 0.012, 0.024, 0.048, 0.081, 0.096, 0.171, 0.192, 0.384, 0.540 and 0.720) were prepared by the co-precipitation method and subjected to five cumulative stages of isothermal treatment in the temperature range from 900 to 1050 °C. The phase evolution of the oxides were investigated quantitatively by the X-ray powder diffraction approach using the Rietveld method of analysis. An almost single phase cubic garnet structure was attained at temperatures as low as 900 °C for specimens with neodymium loading less than ca. 6 at.% with respect to total (Nd + Y) atoms. Isothermal treat…
Mechanical treatment of TiO2 and ZrO2 oxide mixtures
2010
The mixed ZrO2–TiO2 system (5–50 wt% of ZrO2) has been studied to investigate the influence of the mechanical treatment on its physicochemical properties depending on the composition, time of milling (5, 10 and 20 min, r.p.m. 82) and temperature (400, 550 and 700 C). Samples were characterized by Raman spectroscopy, X-ray powder diffraction, Scanning Electron Microscopy coupled with Energy Dispersion X-ray analyzer, High Resolution-Transmission Electron Microscopy and nitrogen adsorption porosimetry. Results show that srilankite (TiZrO4) phase has been produced. No influence of the milling time and temperature on the phase composition is observed. The presence of zirconia increases the ther…